Температура плавления высокотемпературных керамик
| Вещество |
tпл, °C |
| $HfC$ |
$3890 \pm 150$ |
| $TaC$ |
$3880 \pm 150$ |
| $ZrC$ |
3530 |
| $NbC$ |
3480 |
| $HfB_{2}$ |
$3250 \pm 100$ |
| $TiN$ |
3205 |
| $TiC$ |
3147 |
| $TaB_{2}$ |
3100 |
| $TaN$ |
$3087 \pm 50$ |
| $NbB_{2}$ |
3000 |
| $HFN$ |
2982 |
| $ZrN$ |
2982 |
| $TiB_{2}$ |
2980 |
| $ThO_{2}$ |
2950 |
| $ThN$ |
$2630 \pm 50$ |
| $CoO$ |
2603 |
| $NdB_{6}$ |
2540 |
| $SmB_{6}$ |
2540 |
| $Lab_{6}$ |
2530 |
| $Ta_{4}Si$ |
2510 |
| $MgO$ |
2500 |
| $Ta_{5}Si_{3}$ |
2500 |
| $UB_{4}$ |
2495 |
| $SrO$ |
2460 |
| $CeS$ |
2450 |
| $BeO$ |
2440 |
| $Cr_{2}O_{2}$ |
2440 |
| $Nb_{5}Si_{3}$ |
2440 |
| $TaB$ |
2430 |
| $ThS$ |
2425 |
| $TaS$ |
2425 |
| $Nb_{2}N$ |
2420 |
| $Y_{2}O_{3}$ |
2410 |
| $AlN$ |
2400 |
| $U_{2}C$ |
2400 |
| $VB_{2}$ |
$2400 \pm 50$ |
| $WB( \alpha)$ |
$2400 \pm 100$ |
| $UB_{2}$ |
2385 |
| $VN$ |
2360 |
| $MoB$ |
2350 |
| $UC$ |
2315 |
| $La_{2}O_{3}$ |
2310 |
| $YC_{2}$ |
$2300 \pm 50$ |
| $W_{2}B_{5}$ |
$2300 \pm 50$ |
| $BeB_{6}$ |
2300 |
| $YB_{6}$ |
2300 |
| $CaC_{2}$ |
2300 |
| $Th_{2}S$ |
2300 |
| $Th_{4}S_{7}$ |
2300 |
| $NbB$ |
2280 |
| $NbB_{4}$ |
2900 |
| $VC$ |
2810 |
| $HiO_{2}$ |
2790 |
| $W_{2}B$ |
$2770 \pm 80$ |
| $W_{2}C$ |
$2730 \pm 15$ |
| $UO_{2}$ |
2730 |
| $WC$ |
2720 |
| $MoC$ |
2700 |
| $ZrO_{2}$ |
2700 |
| $ZrB_{12}$ |
2680 |
| $YN$ |
2670 |
| $ThC_{2}$ |
$2656 \pm 75$ |
| $ScN$ |
2650 |
| $UN$ |
$2650 \pm 100$ |
| $ScB_{2}$ |
2250 |
| $Mo_{3}B_{2}$ |
2250 |
| $VB$ |
2250 |
| $Zr_{5}Si_{3}$ |
2250 |
| $UC_{2}$ |
2250 |
| $SrB_{6}$ |
2235 |
| $UB_{12}$ |
2235 |
| $CaB_{6}$ |
2230 |
| $BaB_{6}$ |
2230 |
| $Ba_{3}N_{2}$ |
2220 |
| $ThB_{4}$ |
2210 |
| $Be_{3}N_{5}$ |
2205 |
| $BaS$ |
2205 |
| $Be_{3}N_{2}$ |
2200 |
| $Ti_{2}B$ |
2200 |
| $CrB_{2}$ |
$2200 \pm 50$ |
| $Ta Si_{2}$ |
2200 |
| $Nd_{2}S_{3}$ |
2200 |
| $GeB_{6}$ |
2190 |
| $WSi_{2}$ |
2165 |
| $ThB_{6}$ |
2150 |
| $ZrSi$ |
2150 |
| $Mo_{2}B$ |
2140 |
| $NdS$ |
2140 |
| $Ti_{5}Si_{3}$ |
2120 |
| $GdB_{6}$ |
2100 |
| $Th_{3}N_{4}$ |
2100 |
| $MoB_{2}$ |
2100 |
| $La_{2}S_{3}$ |
2100 |
| $V_{3}B_{2}$ |
2070 |
| $Al_{2}O_{3}$ |
2050 |
| $CrB$ |
2050 |
| $Ce_{3}S_{4}$ |
$2050 \pm 75$ |
| $MoSi_{2}$ |
2030 |
| $TIO$ |
2020 |
| $Al_{2}O_{3} \cdot BaO$ |
2000 |